| Título: | Análise química comparativa da qualidade do cimento portland tipo ii, classe 32.5, das fábricas da Matola, Beira e Nacala |
| Autor(es): | Chichango, Edna Celina Alberto |
| Primeiro Orientador: | Kin, Fung Dai |
| metadata.dc.contributor.advisor-co1: | Mabui, Moisés |
| Resumo: | O presente trabalho objectiva avaliar e comparar a qualidade de diferentes amostras de cimento Portland tipo II, classe 32.5, produzido por 3 fábricas de cimento de Moçambique, nomeadamente fábricas da Matola, Beira e Nacala. Para tal 15 amostras de cimento, divididas em 5 amostras por fábrica foram analisadas e os resultados obtidos comparados. Os parâmetros do cimento determinados foram: Fe 2 O 3 , CaO, MgO, Na 2 O, K 2 O, SiO 2 , SO 3 , resíduo insolúvel (RI) e perda ao rubro (PR). Os métodos usados para as análises foram: espectrofotometria de absorção atómica com chama (FAAS), fotometria de chama (FC) e gravimetria. A exactidão dos métodos FAAS e FC foi averiguada através da análise do material de referência, calcário KH, fornecido pelo Laboratório da Direcção Nacional de Geologia (DNG). Verificou-se, a partir dos erros relativos e das taxas de recuperação, que ela variou de boa a muito boa para todos os elementos analisados com excepção de magnésio e ferro. O mesmo se verificou através do test t para comparação da média experimental e teórica cujos resultados, a um nível de confiança de 95%, mostraram evidências de diferenças significativas para o ferro e magnésio. Em termos de precisão, os valores calculados de %RSD demonstram que ela variou de boa a muito boa para quase todas as amostras analisadas por gravimetria, FAAS e FC. Averiguou-se a qualidade das amostras comparando-se os resultados obtidos para cada parâmetro com os teores especificados pelas normas, tendo-se notado que, para grande parte das amostras analisadas os parâmetros determinados cumprem com os requisitos fixados nas normas. Empregando a ANOVA notou-se haver diferenças significativas, entre amostras produzidas em diferentes dias entre os meses de Março a Julho em cada fábrica, para RI, MgO e SO 3 . Comparou-se a qualidade do cimento das diferentes fábricas através da ANOVA e notou-se que, com excepção do potássio, não há diferença significativa entre os teores dos parâmetros analisados nas amostras das diferentes fábricas testadas. Deste modo, o cimento produzido pelas 3 fábricas pode ser usado para construção civil em estruturas cuja exposição ao ataque de sulfatos seja moderada. |
| Abstract: | The present work aims to evaluate and compare the quality of different cement samples Portland type II, class 32.5, produced by 3 cement factories in Mozambique, namely factories in Matola, Beira and Nacala. For this, 15 cement samples, divided 5 samples per factory were analyzed and the results obtained compared. (TRADUÇÃO NOSSA) The cement parameters determined were: Fe 2 O 3, CaO, MgO, Na 2 O, K 2 O, SiO 2, SO 3, insoluble residue (IR) and red loss (PR). The methods used for the analyzes were: flame atomic absorption spectrophotometry (FAAS), flame photometry (FC) and gravimetry. The accuracy of the FAAS and FC methods was verified through the analysis of the reference material, KH limestone, supplied by the Laboratory of the National Directorate of Geology (DNG). It was found, from relative errors and recovery rates, which ranged from good to very good for all elements analyzed with the exception of magnesium and iron. The same was verified through test t to compare the experimental and theoretical average whose results, at a level of 95% confidence, showed evidence of significant differences for iron and magnesium. In terms of accuracy, the calculated% RSD values demonstrate that it varied from good to very good for almost all samples analyzed by gravimetry, FAAS and FC. The quality of the samples was investigated by comparing the results obtained for each parameter with the contents specified by the norms, having noticed that, for most of the samples analyzed the parameters determined comply with the requirements set out in the standards. Using ANOVA it was noted that there are significant differences between samples produced in different days between the months of March to July in each factory, for IR, MgO and SO 3. The quality of the cement from the different factories was compared using ANOVA and it was noted that, with the exception of potassium, there is no significant difference between the levels of the parameters analyzed in the samples of the different factories tested. In this way, the cement produced by 3 factories can be used for civil construction in structures whose exposure to attack by sulphates is moderate. |
| Palavras-chave: | Cimento Portland Qualidade Moçambique Análise química |
| CNPq: | Ciências Exactas e da Terra Química |
| Idioma: | por |
| País: | Moçambique |
| Editor: | Universidade Eduardo Mondlane |
| Sigla da Instituição: | UEM |
| metadata.dc.publisher.department: | Faculdade de Ciências Departamento de Quίmica |
| Tipo de Acesso: | Acesso Aberto |
| URI: | http://localhost:8080/xmlui/handle/123456789/163 |
| Data do documento: | 1-Abr-2010 |
| Aparece nas coleções: | FC - Química Industrial |
Arquivos associados a este item:
| Arquivo | Descrição | Tamanho | Formato | |
|---|---|---|---|---|
| 2010 - Chichango, Edna Celina Alberto.pdf | 2.28 MB | Adobe PDF | Visualizar/Abrir |
Os itens no repositório estão protegidos por copyright, com todos os direitos reservados, salvo quando é indicado o contrário.